Poly Vinyl Formal Pvf Foam

Through the help of images taken by a scanning electron microscope the formation process of the present pvf foam will be discussed in terms of the spinodal decomposition sd phase separation principle.

Poly vinyl formal pvf foam.

The pvf foams could be used as sound absorbing materials because of the open cell multiporous structures. The modulus of the composite increased 1857 and the highest volume expansivity reached 2150. And the highest α value of 0 98 was obtained at 2000 hz for pvf 3 0. Formvar used to be the registered trade name of the polyvinyl formal resin produced by monsanto chemical company in st.

Morphology observation showed that the porous structure of pvf foams was successfully created using water as the blowing agent and it was strongly affected by the crosslinking agent and polymer concentration leading to an easily tuned pore size from hundreds of microns to few microns. A very broad characteristic absorption peak centred at about 3490. 3 1 1 polyvinyl formal pvf. Outstanding solution absorbing performance unique high rate hydroexpansivity and promising biocompatibility.

Scanning electron microscopy showed that the pvf foams had two kinds of pore structures closed and open cell. The sound absorption coefficient α of the pvf foam largely increased with the decreasing pore size especially in the frequency range of 800 2500 hz. Find sigma aldrich 182680 msds related peer reviewed papers technical documents similar products more at sigma aldrich. Developed a double crosslinking sodium alginate sa polyvinyl formal pvf composite with ipn structure.

Ir spectroscopy results on pvf and its polymeric subunits pva and pvac are discussed in detail. By changing the concentration from 10 to 20 wt of pva solution pvf foams were successfully obtained. The state key laboratory of polymer materials engineering polymer research institute of sichuan university chengdu 610065 china new materials r d center institute of chemical material china academy of engineering physics mianyang 621900 china. The formation of the formal was.

Poly vinyl formal pvf of 90 acetalization was prepared by acid catalysed homogeneous formalization of pva of molecular weight 14 000 with paraformaldehyde.